ATB-30,,試拌3.2油石比,,,,,,,,,,,,,

油石比（%）,,3.3,瀝青用量（%）,3.2,,瀝青密度,1.009,,,,,,,γsa合成表觀相對密度,2.755

序號,平均厚度mm,空氣中質(zhì)量（g）,水中質(zhì)量（g）,表干質(zhì)量（g）,吸水率（%）,毛體積密度（相對）,最大理論密度（相對）,孔隙率（%）,礦料間隙率（%）,飽和度（%）,穩(wěn)定度（KN）,流值（0.1mm）,馬氏模數(shù)（%）,γsb合成毛體積相對密度,2.692

1,,4057.3,2419.7,4077.8,1.2,2.447,2.585,5.3,12.0,55.7,19.45,26.7,0.7,合成礦料有效相對密度（γse）反算,2.725

2,,4056.8,2417.2,4081.2,1.5,2.438,2.585,5.7,12.3,54.1,20.12,28.6,0.7,合成礦料瀝青吸收系數(shù)（C）,0.709093792

3,,4047.9,2421.3,4079.6,1.9,2.441,2.585,5.6,12.2,54.6,18.78,29.1,0.6,合成礦料吸水率（Ws）%,0.846165026

4,,4059.2,2417.0,4084.7,1.5,2.434,2.585,5.8,12.5,53.4,19.32,23.3,0.8,合成礦料有效相對密度（γse）記算,2.737

5,,4053.1,2426.6,4083.6,1.8,2.446,2.585,5.4,12.1,55.5,18.98,25.8,0.7,最大理論密度計算所得γti,2.595

6,,4056.1,2419.1,4082.1,1.6,2.439,2.585,5.6,12.3,54.3,19.23,27.1,0.7,瀝青結(jié)合料被集料吸收的比例（Pba）,23.660

平均,,,,,1.6,2.441,,5.6,12.2,54.6,19.31,26.8,0.7,有效瀝青用量,2.97

,,,,,,,,,,,,,,,,

油石比（%）,,3.6,瀝青用量（%）,3.5,,瀝青密度,1.009,,,,,,,γsa合成表觀相對密度,2.755

序號,平均厚度mm,空氣中質(zhì)量（g）,水中質(zhì)量（g）,表干質(zhì)量（g）,吸水率（%）,毛體積密度（相對）,最大理論密度（相對）,孔隙率（%）,礦料間隙率（%）,飽和度（%）,穩(wěn)定度（KN）,流值（0.1mm）,馬氏模數(shù)（%）,γsb合成毛體積相對密度,2.692

1,,4053.3,2425.7,4069.4,1.0,2.466,2.576,4.3,11.6,63.3,21.20,29.8,0.7,合成礦料有效相對密度（γse）反算,2.728

2,,4064.8,2432.1,4079.1,0.9,2.468,2.576,4.2,11.5,63.8,22.40,27.8,0.8,合成礦料瀝青吸收系數(shù)（C）,0.709093792

3,,4059.5,2428.3,4073.8,0.9,2.467,2.576,4.2,11.6,63.5,23.70,30.1,0.8,合成礦料吸水率（Ws）%,0.846165026

4,,4066.9,2430.3,4080.8,0.8,2.464,2.576,4.3,11.7,62.9,21.90,27.4,0.8,合成礦料有效相對密度（γse）記算,2.737

5,,4052.3,2423.3,4069.2,1.0,2.462,2.576,4.4,11.7,62.4,23.60,28.5,0.8,最大理論密度計算所得γti,2.583

6,,4047.8,2423.2,4061.3,0.8,2.471,2.576,4.1,11.4,64.4,22.10,26.9,0.8,瀝青結(jié)合料被集料吸收的比例（Pba）,23.660

平均,,,,,0.9,2.466,,4.2,11.6,63.4,22.48,28.4,0.8,有效瀝青用量,3.25

,,,,,,,,,,,,,,,,

油石比（%）,,3.9,瀝青用量（%）,3.8,,瀝青密度,1.009,,,,,,,γsa合成表觀相對密度,2.755

序號,平均厚度mm,空氣中質(zhì)量（g）,水中質(zhì)量（g）,表干質(zhì)量（g）,吸水率（%）,毛體積密度（相對）,最大理論密度（相對）,孔隙率（%）,礦料間隙率（%）,飽和度（%）,穩(wěn)定度（KN）,流值（0.1mm）,馬氏模數(shù)（%）,γsb合成毛體積相對密度,2.692

1,,4056.2,2425.9,4070.1,0.8,2.467,2.567,3.9,11.8,67.2,20.12,30.1,0.7,合成礦料有效相對密度（γse）反算,2.731

2,,4045.1,2416.3,4059.3,0.9,2.462,2.567,4.1,12.0,66.0,21.35,32.1,0.7,合成礦料瀝青吸收系數(shù)（C）,0.709093792

3,,4062.3,2430.1,4074.1,0.7,2.471,2.567,3.7,11.7,68.1,22.39,29.8,0.8,合成礦料吸水率（Ws）%,0.846165026

4,,4041.8,2419.2,4056.9,0.9,2.468,2.567,3.8,11.8,67.4,21.86,28.7,0.8,合成礦料有效相對密度（γse）記算,2.737

5,,4056.4,2417.7,4064.6,0.5,2.463,2.567,4.0,12.0,66.3,20.19,30.2,0.7,最大理論密度計算所得γti,2.572

6,,4067.1,2422.3,4076.3,0.6,2.459,2.567,4.2,12.1,65.4,23.32,31.2,0.7,瀝青結(jié)合料被集料吸收的比例（Pba）,23.660

平均,,,,,0.7,2.465,,4.0,11.9,66.7,21.54,30.4,0.7,有效瀝青用量,3.53

,,,,,,,,,,OAC1(%),3.4,,,,

油石比,,毛體積密度,孔隙率,礦料間隙率,飽和度,穩(wěn)定度,流值,,,OAC2(%),3.3,,,,

3.1,,2.441,5.6,12.2,54.6,26.8,26.8,,,OAC(%),3.3,,,,

3.4,,2.466,4.2,11.6,63.4,22.48,28.4,,,,,,,